Comb-shaped copolymers based on acryoyldimethyl taurine acid

ABSTRACT

The invention provides water-soluble or water-swellable copolymers obtainable by free-radical copolymerization of  
     A) acryloyidimethyltaurine and/or acryloyldimethyltaurates,  
     B) if desired, one or more other olefinically unsaturated, noncationic comonomers,  
     C) if desired, one or more olefinically unsaturated, cationic comonomers,  
     D) if desired, (a) silicon-containing component(s),  
     E) if desired, (a) fluorine-containing component(s),  
     F) if desired, one or more macromonomers,  
     G) the copolymerization taking place in the presence or absence of at least one polymeric additive,  
     H) with the proviso that component A) is copolymerized with at least two components selected from at least two of the groups C) to F).

[0001] The present invention relates to comb copolymers based on acryloyldimethyltaurine and/or acryloyldimethyltaurates.

[0002] In recent years water-soluble polymers have acquired a continually increasing importance in industry and science. In volume terms, polyelectrolytes are occupying a very large proportion of the overall annual production. They find application, for example, in paper processing, in the laundry detergents industry, in textile processing, in petroleum extraction or as important base materials for cosmetics.

[0003] In the cosmetics sector a key role is assigned to polyelectrolytes. Besides water-soluble surface-active substances there is a high demand in this sector for systems which thicken oil and water. Thickeners of this kind, particularly the “superabsorbents” prepared on the basis of polyacrylic acid, have progressed since their development in the 1970s to become a pillar of the hygiene sector. In their crosslinked versions, partly or fully neutralized polyacrylic acids and their water-soluble copolymers are employed in numerous cosmetic formulations as bodying agents. The diversity of possible structures and the diverse possible applications associated therewith are manifested not least in a host of patents filed worldwide since the mid-1970s.

[0004] In the 1990s, innovative thickeners based on 2-acrylamido-2-methyl-1-propane-sulfonic acid (AMPS) and their salts were introduced into the market (EP 816 403 and WO 98/00094). In both homopolymer and copolymer form (®Aristoflex AVC, Clariant GmbH) such thickeners are superior in many respects to the corresponding polycarboxylates (Carbopols). For example, thickener systems based on AMPS display outstanding properties in pH ranges below pH 6, i.e., in a pH range in which it is no longer possible to operate with conventional polycarboxylate thickeners. Moreover, the microgel structure inherent in the acryloyldimethyltaurine thickeners leads to a particularly pleasant skin sensation.

[0005] The ease of processing and the favorable toxicological profile of the principal monomer imbue these thickeners with a high application potential.

[0006] Over recent years representatives of a new thickener design have entered the market. In these thickeners, two different properties have been combined in one polymer, thereby opening up new fields of application. Thickening emulsifiers or dispersants are but two examples of this new class of substance. Brand names that may be mentioned include the Pemulens® TR-1 and TR-2 from BF Goodrich or the Aculyn® products from Rohm & Haas. All existing versions are based on hydrophobically modified versions of the conventional polyacrylates.

[0007] Surprisingly it has been found that a new class of copolymers based on acryloyldimethyltaurine (AMPS) gives the user the possibility of combining properties of nonpolar moieties, such as alkyl chains or silicone-containing structures, with hydrophilic structural units, such as polyglycols or polyelectrolytes, thereby providing the user in turn with completely new opportunities in formulation technology. The use of the polyfunctional polymers of the invention permits substantial formula simplification for manufacturers of cosmetics, for example.

[0008] The invention provides water-soluble or water-swellable copolymers obtainable by free-radical copolymerization of

[0009] A) acryloyldimethyltaurine and/or acryloyldimethyltaurates,

[0010] B) if desired, one or more other olefinically unsaturated, noncationic, optionally crosslinking comonomers containing at least one oxygen, nitrogen, sulfur or phosphorus atom and possessing a molecular weight of less than 500 g/mol,

[0011] C) if desired, one or more olefinically unsaturated, cationic comonomers containing at least one oxygen, nitrogen, sulfur or phosphorus atom and possessing a molecular weight of less than 500 g/mol,

[0012] D) if desired, one or more at least monofunctional, silicon-containing components capable of free-radical polymerization,

[0013] E) if desired, one or more at least monofunctional, fluorine-containing components capable of free-radical polymerization,

[0014] F) if desired, one or more mono- or polyolefinically unsaturated, optionally crosslinking macromonomers each possessing at least one oxygen, nitrogen, sulfur or phosphorus atom and having a number-average molecular weight of greater than or equal to 200 g/mol, the macromonomers not being a silicon-containing component D) or fluorine-containing component E),

[0015] G) the copolymerization taking place in the presence or absence of at least one polymeric additive having number-average molecular weights of from 200 g/mol to 10⁹ g/mol,

[0016] H) with the proviso that component A) is copolymerized with at least two components selected from at least two of the groups C) to F).

[0017] The copolymers of the invention preferably possess a molecular weight of from 10³ g/mol to 10⁹ g/mol, more preferably from 10⁴ to 10⁷ g/mol, very preferably from 5*10⁴ to 5*10⁶ g/mol.

[0018] The acryloyldimethyltaurates can be the organic or inorganic salts of acryloyldimethyltaurine. Preference is given to the Li⁺, Na⁺, K⁺, Mg⁺⁺, Ca⁺⁺, Al⁺⁺⁺ and/or NH₄ ⁺ salts. Likewise preferred are the monoalkylammonium, dialkylammonium, trialkylammonium and/or tetraalkylammonium salts, in which the alkyl substituents of the amines may independently of one another be (C₁-C₂₂)-alkyl radicals or (C₂-C₁₀)-hydroxyalkyl radicals. Preference is also given to mono- to triethoxylated ammonium compounds with a different degree of ethoxylation. It should be noted that the invention also embraces mixtures of two or more of the abovementioned representatives.

[0019] The degree of neutralization of the acryloyldimethyltaurine can be between 0 and 100%, particular preference being given to a degree of neutralization of more than 80%.

[0020] Based on the total mass of the copolymers, the amount of acryloyldimethyltaurine and/or acryloyldimethyltaurates is at least 0.1% by weight, preferably from 20 to 99.5% by weight, more preferably from 50 to 98% by weight.

[0021] As comonomers B) it is possible to use all olefinically unsaturated noncationic monomers whose reaction parameters allow copolymerization with acryloyldimethyltaurine and/or acryloyldimethyltaurates in the respective reaction media. Preferred comonomers B) are unsaturated carboxylic acids and their anhydrides and salts, and also their esters with aliphatic, olefinic, cycloaliphatic, arylaliphatic or aromatic alcohols having a carbon number of from 1 to 22.

[0022] Particularly preferred unsaturated carboxylic acids are acrylic acid, methacrylic acid, styrenesulfonic acid, maleic acid, fumaric acid, crotonic acid, itaconic acid, and senecic acid.

[0023] Preferred counterions are Li⁺, Na⁺, K⁺, Mg⁺⁺, Ca⁺⁺, Al⁺⁺⁺, NH₄ ⁺, monoalkylammonium, dialkylammonium, trialkylammonium and/or tetraalkylammonium radicals, in which the alkyl substituents of the amines independently of one another can be (C₁-C₂₂)-alkyl radicals or (C₂-C₁₀)-hydroxyalkyl radicals. It is additionally possible to employ mono- to triethoxylated ammonium compounds with a different degree of ethoxylation. The degree of neutralization of the carboxylic acids can be between 0 and 100%. Further preferred comonomers B) are open-chain N-vinyl amides, preferably N-vinylformamide (VIFA), N-vinylmethylformamide, N-vinylmethylacetamide (VIMA) and N-vinylacetamide; cyclic N-vinyl amides (N-vinyl lactams) with a ring size of 3 to 9, preferably N-vinylpyrrolidone (NVP) and N-vinylcaprolactam; amides of acrylic and methacrylic acid, preferably acrylamide, methacrylamide, N,N-dimethylacrylamide, N,N-diethylacrylamide, and N,N-diisopropylacrylamide; alkoxylated acrylamides and methacrylamides, preferably hydroxyethyl methacrylate, hydroxymethylmethacrylamide, hydroxyethylmethacrylamide, hydroxypropylmethacrylamide, and mono [2-(methacryloyloxy)ethyl] succinate; N,N-dimethylamino methacrylate; diethylaminomethyl methacrylate; acrylamido- and methacrylamidoglycolic acid; 2- and 4-vinylpyridine; vinyl acetate; glycidyl methacrylate; styrene; acrylonitrile; vinyl chloride; stearyl acrylate; lauryl methacrylate; vinylidene chloride; and/or tetrafluoroethylene. Likewise suitable comonomers B) are inorganic acids and their salts and esters. Preferred acids are vinylphosphonic acid, vinylsulfonic acid, allylphosphonic acid, and methallylsulfonic acid.

[0024] The weight fraction of the comonomers B), based on the total mass of the copolymers, can be from 0 to 99.7% by weight and is preferably from 0.5 to 80% by weight, more preferably from 2 to 50% by weight.

[0025] Suitable comonomers C) include all olefinically unsaturated monomers with cationic charge which are capable of forming copolymers with acryloyldimethyl-taurine or its salts in the chosen reaction media. The resulting distribution of the cationic charges across the chains can be random, alternating, blocklike or gradientlike. It may be noted that the cationic comonomers C) also comprehend those which bear the cationic charge in the form of a betaine structure.

[0026] Comonomers C) for the purposes of the invention are also amino-functionalized precursors which can be converted into their corresponding quaternary derivatives by polymer-analogous reactions (e.g., reaction with DMS). Particularly preferred comonomers C) are diallyidimethylammonium chloride (DADMAC), [2-(methacryloyloxy)ethyl]trimethylammonium chloride (MAPTAC), [2-(acryloyloxy)ethyl]trimethylammonium chloride, [2-methacrylamidoethyl]trimethylammonium chloride, [2-(acrylamido)ethyl]trimethylammonium chloride, N-methyl-2-vinylpyridinium chloride and/or N-methyl4-vinylpyridinium chloride.

[0027] The weight fraction of the comonomers C), based on the total mass of the copolymers, is preferably from 0.1 to 99.8% by weight, more preferably from 0.5 to 30% by weight, and very preferably from 1 to 20% by weight.

[0028] Suitable polymerizable silicon-containing components D) are all compounds which are olefinically at least monounsaturated and capable of free-radical copolymerization under the reaction conditions chosen in each case. The distribution of the individual silicone-containing monomers across the polymer chains which form need not necessarily be random. The invention also embraces the formation, for example, of blocklike (including multiblock) or gradientlike structures. Combinations of two or more different silicone-containing representatives are also possible. The use of silicone-containing components having two or more polymerization-active groups leads to the construction of branched or crosslinked structures.

[0029] Preferred silicon-containing components are those of formula (I).

R¹—Z—[(Si(R³R⁴)—O—)_(w)—(Si(R⁵R⁶)—O)_(x)—]—R²  (I)

[0030] In this formula R¹ represents a polymerizable function from the group of the vinylically unsaturated compounds which is suitable for the synthesis of polymeric structures by a free-radical route. R¹ represents preferably a vinyl, allyl, methallyl, methylvinyl, acryloyl (CH₂═CH—CO—), methacryloyl (CH₂═C[CH₃]—CO—), crotonyl, senecionyl, itaconyl, maleyl, fumaryl or styryl radical.

[0031] The attachment of the silicone-containing polymer chain to the reactive end group R¹ requires a suitable chemical bridge Z. Preferred bridges Z are —O—, —((C₁-C₅₀)alkylene)-, —((C₆-C₃₀)arylene)-, —((C₅-C₈)cycloalkylene)—, —((C₁-C₅₀)alkenylene)-, -(polypropylene oxide)_(n)-, -(polyethylene oxide)_(o)-, -(polypropylene oxide)_(n)(polyethylene oxide)_(o)-, where n and o independently of one another denote numbers from 0 to 200 and the distribution of the EO/PO units can be random or in the form of blocks. Further suitable bridge groups Z are —((C₁-C₁₀)alkenyl)-(Si(OCH₃)₂)— and —(Si(OCH₃)₂)—.

[0032] The polymeric central moiety is represented by silicone-containing repeating units.

[0033] The radicals R³, R⁴, R⁵, and R⁶ denote independently of one another —CH₃, —O—CH₃, —C₆H₅ or —O—C₆H₅.

[0034] The indices w and x represent stoichiometric coefficients which amount independently of one another to from 0 to 500, preferably 10 to 250.

[0035] The distribution of the repeating units across the chain can be not only purely random but also blocklike, alternating or gradientlike.

[0036] R² can on the one hand symbolize an aliphatic, olefinic, cycloaliphatic, arylaliphatic or aromatic (C₁-C₅₀) hydrocarbon radical (linear or branched) or stand for —OH, —NH₂, —N(CH₃)₂, —R⁷ or the structural unit [—Z—R¹]. The definition of the two variables Z and R¹ has already been explained. R⁷ stands for further Si-containing groups. Preferred R⁷ radicals are —O—Si(CH₃)₃, —O—Si(Ph)₃, —O—Si(O—Si(CH₃)₃)₂CH₃ and —O—Si(O—Si(Ph)₃)₂Ph.

[0037] If R² is an element of the group [—Z—R¹] the monomers in question are difunctional monomers which can be used to crosslink the polymer structures which form. Formula (I) describes not only silicone-containing polymer species with vinylic functionalization and a polymer-typical distribution, but also defined compounds having discrete molecular weights.

[0038] Particularly preferred silicone-containing components are the following such components with acrylic or methacrylic modification:

[0039] methacryloyloxypropyldimethylsilyl-endblocked polydimethylsiloxanes (f=2 to 500)

[0040] methacryloyloxypropyl-endblocked polydimethylsiloxanes (f=2 to 500)

[0041] vinyldimethoxysilyl-endblocked polydimethylsiloxanes (f=2-500)

[0042] Based on the total mass of the copolymers, the weight fraction of the comonomers D) can be from 0.1 to 99.8% by weight, preferably from 0.1 to 50% by weight, more preferably from 0.2 to 40% by weight, very preferably from 0.5 to 30% by weight.

[0043] Suitable polymerizable fluorine-containing components E) include all compounds which are olefinically at least monounsaturated and which are capable of free-radical copolymerization under the reaction conditions chosen in each case. The distribution of the individual fluorine-containing monomers across the polymer chains which form need not necessarily be random. The invention also embraces the formation of blocklike (including multiblock) or gradientlike structures, for example. Combinations of two or more different fluorine-containing components E) are also possible, it being clear to the expert that monofunctional representatives lead to the formation of comb-shaped structures while di-, tri-, or polyfunctional components E) lead to structures which are at least partly crosslinked.

[0044] Preferred fluorine-containing components E) are those of formula (II).

R¹—Y—C_(r)H_(2r)C_(s)F_(2s)CF₃  (II)

[0045] In this formula R¹ represents a polymerizable function from the group of the vinylically unsaturated compounds which is suitable for the construction of polymeric structures by a free-radical route. R¹ is preferably a vinyl, allyl, methallyl, methylvinyl, acryloyl (CH₂═CH—CO—), methacryloyl (CH₂═C[CH₃]—CO—), crotonyl, senecionyl, itaconyl, maleyl, fumaryl or styryl radical, more preferably an acryloyl or methacryloyl radical.

[0046] The attachment of the fluorine-containing group to the reactive end group R¹ requires a suitable chemical bridge Y. Preferred bridges Y are —O—, —C(O)—, —C(O)—O—, —S—, —O—CH₂—CH(O—)—CH₂OH, —O—CH₂—CH(OH)—CH₂—O—, —O—SO₂—O—, —O—S(O)—O—, —PH—, —P(CH₃)—, —PO₃—, —NH—,—N(CH₃)—, —O—(C₁-C₅₀alkyl-O—, —O-phenyl-O—, —O-benzyl-O—, —O—(C₅-C₈)cycloalkyl-O—, —O—(C₁-C₅₀)alkenyl-O—, —O—(CH(CH₃)—CH₂—O)_(n)—, —O—(CH₂—CH₂—O)n—, and —O—([CH—CH₂—O]_(n)—[CH₂—CH₂—O]_(m))_(o)—,

[0047] where n, m, and o independently of one another denote numbers from 0 to 200 and the distribution of the EO and PO units can be random or in the form of blocks.

[0048] r and s are stoichiometric coefficients which independently of one another denote numbers from 0 to 200.

[0049] Particularly preferred fluorine-containing components are

[0050] perfluorohexylethanol methacrylate,

[0051] perfluorohexoylpropanol methacrylate,

[0052] perfluoroctylethanol methacrylate,

[0053] perfluoroctylpropanol methacrylate,

[0054] perfluorohexylethanolyl polyglycol ether methacrylate,

[0055] perfluorohexoylpropanolyl poly[ethylglycol-co-propylene glycol ether] acrylate,

[0056] perfluoroctylethanolyl poly[ethylglycol-block-co-propylene glycol ether]

[0057] methacrylate, and/or

[0058] perfluoroctylpropanolyl polypropylene glycol ether methacrylate.

[0059] Based on the total mass of the copolymers, the weight fraction of the comonomers E) can be from 0.1 to 99.8% by weight, preferably from 0.1 to 50% by weight, more preferably from 0.2 to 30% by weight, very preferably from 0.5 to 20% by weight.

[0060] The macromonomers F) are at least singly olefinically functionalized polymers having one or more discrete repeating units and a number-average molecular weight of greater than or equal to 200 g/mol. In the copolymerization it is also possible to use mixtures of chemically different macromonomers F). The macromonomers are polymeric structures composed of one or more repeating units and have a molecular weight distribution characteristic of polymers.

[0061] Preferred macromonomers F) are compounds of formula (III).

R¹—Y—[(A)_(v)—(B)_(w)—(C)_(x)—(D)_(z)]—R²  (III)

[0062] R¹ represents a polymerizable function from the group of the vinylically unsaturated compounds which are suitable for constructing polymeric structures by a free-radical route. Preferably R¹ is a vinyl, allyl, methallyl, methylvinyl, acryloyl (CH₂═CH—CO—), methacryloyl (CH₂═C[CH₃]—CO—), crotonyl, senecionyl, itaconyl, maleyl, fumaryl or styryl radical.

[0063] Attachment of the polymer chain to the reactive end group requires a suitable bridging group Y. Preferred bridges Y are —O—, —C(O)—, —C(O)—O—, —S—, —O—CH₂—CH(O—)—CH₂OH, —O—CH₂—CH(OH)—CH₂O—, —O—SO₂—O—, —O—SO₂—O—, —O—SO—O—, —PH—, —P(CH₃)—, —PO₃—, —NH—, and —N(CH₃)—, more preferably —O—.

[0064] The polymeric central moiety of the macromonomer is represented by the discrete repeating units A, B, C, and D. Preferred repeating units A, B, C, and D are derived from acrylamide, methacrylamide, ethylene oxide, propylene oxide, AMPS, acrylic acid, methacrylic acid, methyl methacrylate, acrylonitrile, maleic acid, vinyl acetate, styrene, 1,3-butadiene, isoprene, isobutene, diethylacrylamide, and diisopropylacrylamide.

[0065] The indices v, w, x, and z in formula (III) represent the stoichiometric coefficients relating to the repeating units A, B, C, and D. v, w, x, and z amount independently of one another to from 0 to 500, preferably 1 to 30, it being necessary for the sum of the four coefficients on average to be ≧1.

[0066] The distribution of the repeating units over the macromonomer chain can be random, blocklike, alternating or gradientlike.

[0067] R² denotes a linear or branched aliphatic, olefinic, cycloaliphatic, arylaliphatic or aromatic (C₁-C₅₀) hydrocarbon radical, OH, —NH₂, —N(CH₃)₂ or is the structural unit [—Y—R¹].

[0068] In the case of R² being [—Y—R¹] the macromonomers in question are difunctional and suitable for crosslinking the copolymers.

[0069] Particularly preferred macromonomers F) are acrylically or methacrylically monofunctionalized alkyl ethoxylates of formula (IV).

[0070] R³, R⁴, R⁵, and R⁶ are independently of one another hydrogen or n-aliphatic, iso-aliphatic, olefinic, cycloaliphatic, arylaliphatic or aromatic (Cl-C₃₀) hydrocarbon radicals.

[0071] Preferably R³ and R⁴ are H or —CH₃, more preferably H; R⁵is H or —CH₃; and R⁶ is an n-aliphatic, iso-aliphatic, olefinic, cycloaliphatic, arylaliphatic or aromatic (C₁-C₃₀) hydrocarbon radical. v and w are in turn the stoichiometric coefficients relating to the ethylene oxide units (EO) and propylene oxide units (PO). v and w amount independently of one another to from 0 to 500, preferably 1 to 30, it being necessary for the sum of v and w to be on average ≧1. The distribution of the EO and PO units over the macromonomer chain can be random, blocklike, alternating or gradientlike. Y stands for the abovementioned bridges, preferably —O—.

[0072] Particularly preferred macromonomers F) have the following structure in accordance with formula (IV): Name R³ R⁴ R⁵ R⁶ v w ® LA-030 H H —CH₃ -lauryl 3 0 methacrylate ® LA-070 H H —CH₃ -lauryl 7 0 methacrylate ® LA-200 H H —CH₃ -lauryl 20 0 methacrylate ® LA-250 H H —CH₃ -lauryl 25 0 methacrylate ® T-080 methacrylate H H —CH₃ -talc 8 0 ® T-080 acrylate H H H -talc 8 0 ® T-250 methacrylate H H —CH₃ -talc 25 0 ® T-250 crotonate —CH₃ H —CH₃ -talc 25 0 ® OC-030 H H —CH₃ -octyl 3 0 methacrylate ® OC-105 H H —CH₃ -octyl 10 5 methacrylate ® Behenyl-010- H H H -behenyl 10 0 methylaryl ® Behenyl-020- H H H -behenyl 20 0 methylaryl ® Behenyl-010- —CH₃ —CH₃ H -behenyl 10 0 senecionyl ® PEG-440 diacrylate H H H -acryloyl 10 0 ® B-11-50 H H —CH₃ -butyl 17 13 methacrylate ® MPEG-750 H H —CH₃ -methyl 18 0 methacrylate ® P-010 acrylate H H H -phenyl 10 0 ® O-050 acrylate H H H -oleyl 5 0

[0073] The molecular weight of the macromonomers F) is preferably from 200 g/mol to 10⁶ g/mol, more preferably from 150 to 10⁴ g/mol, and very preferably from 200 to 5000 g/mol.

[0074] Based on the total mass of the copolymers, the weight fraction of the macromonomer F) can be from 0.1 to 99.8% by weight, more preferably from 2 to 90% by weight, very preferably from 5 to 80% by weight.

[0075] Preferred copolymers are those obtainable by copolymerizing at least components A), C), and D).

[0076] Further preferred copolymers are those obtainable by copolymerizing at least components A), C), and E).

[0077] Further preferred copolymers are those obtainable by copolymerizing at least components A), C), and F).

[0078] Further preferred copolymers are those obtainable by copolymerizing at least components A), D), and F).

[0079] Further preferred copolymers are those obtainable by copolymerizing at least components A), E), and F).

[0080] Further preferred copolymers are those obtainable by copolymerizing at least components A), B), D), and F).

[0081] Further preferred copolymers are those obtainable by copolymerizing at least components A), B), C), D), and F).

[0082] In one preferred embodiment the copolymerization is conducted in the presence of at least one polymeric additive G), the additive G) being added wholly or partly in solution to the polymerization medium before the actual copolymerization. The use of two or more additives G) is likewise in accordance with the invention. Crosslinked additives G) may likewise be used.

[0083] The additives G) or mixtures thereof must only be wholly or partly soluble in the chosen polymerization medium. During the actual polymerization step the additive G) has a number of functions. On the one hand it prevents the formation of overcrosslinked polymer fractions in the copolymer which forms in the actual polymerization step, and on the other hand the additive G) is statistically attacked by active free radicals in accordance with the very well-known mechanism of graft copolymerization. Depending on the particular additive G), this results in greater or lesser fractions of the additive being incorporated into the copolymers. Moreover, suitable additives G) possess the property of altering the solution parameters of the copolymers which form during the free-radical polymerization reaction in such a way that the average molecular weights are shifted to higher values. As compared with analogous copolymers prepared without the addition of the additives G), those prepared with the addition of additives G) advantageously exhibit a significantly higher viscosity in aqueous solution.

[0084] Preferred additives G) are homopolymers and copolymers which are soluble in water and/or alcohols. The term “copolymers” also comprehends those having more than two different monomer types.

[0085] Particularly preferred additives G) are homopolymers and copolymers of N-vinyl-formamide, N-vinylacetamide, N-vinylpyrrolidone, ethylene oxide, propylene oxide, acryloyldimethyltaurine, N-vinylcaprolactam, N-vinylmethylacetamide, acrylamide, acrylic acid, methacrylic acid, N-vinylmorpholide, hydroxyethyl methacrylate, diallyldimethylammonium chloride (DADMAC) and/or

[0086] [2-(methacryloyloxy)ethyl]trimethylammonium chloride (MAPTAC); polyalkylene glycols and/or alkylpolyglycols.

[0087] Particularly preferred additives G) are polyvinylpyrrolidones (e.g., K15®, K20® and K30® from BASF), poly(N-vinylformamides), poly(N-vinylcaprolactams), and copolymers of N-vinylpyrrolidone, N-vinylformamide and/or acrylic acid, which may also have been partly or fully hydrolyzed.

[0088] The molecular weight of the additives G) is preferably from 10² to 10⁷ g/mol, more preferably from 0.5*10⁴ to 10⁶ g/mol.

[0089] The amount in which the polymeric additive G) is used, based on the total mass of the monomers to be polymerized during the copolymerization, is preferably from 0.1 to 90% by weight, more preferably from 1 to 20% by weight, and with particular preference from 1.5 to 10% by weight.

[0090] In a further preferred embodiment the copolymers of the invention are crosslinked, i.e., they contain comonomers having at least two polymerizable vinyl groups. Preferred crosslinkers are methylenebisacrylamide; methylenebismethacrylamide; esters of unsaturated monocarboxylic and polycarboxylic acids with polyols, preferably di-acrylates and tri-acrylates and -methacrylates, preferably butanediol and ethylene glycol diacrylate and -methacrylate, trimethylolpropane triacrylate (TMPTA) and trimethylolpropane trimethacrylate (TMPTMA); allyl compounds, preferably allyl (meth)acrylate, triallyl cyanurate, diallyl maleate, polyallyl esters, tetraallyloxyethane, triallylamine, tetraallylethylenediamine; allyl esters of phosphoric acid; and/or vinylphosphonic acid derivatives.

[0091] A particularly preferred crosslinker is trimethylolpropane triacrylate (TMPTA). The weight fraction of crosslinking comonomers, based on the total amount of the copolymers, is preferably up to 20% by weight, more preferably from 0.05 to 10% by weight, and with particular preference from 0.1 to 7% by weight.

[0092] The polymerization medium used may comprise all organic or inorganic solvents which have a very substantially inert behavior with respect to free-radical polymerization reactions and which advantageously allow the formation of medium or high molecular weights. Those used preferably include water; lower alcohols; preferably methanol, ethanol, propanols, iso-, sec- and t-butanol, very preferably t-butanol; hydrocarbons having 1 to 30 carbon atoms, and mixtures of the aforementioned compounds.

[0093] The polymerization reaction takes place preferably in the temperature range between 0 and 150° C., more preferably between 10 and 100° C., either at atmospheric pressure or under elevated or reduced pressure. If desired the polymerization may also be performed under an inert gas atmosphere, preferably under nitrogen.

[0094] In order to initiate the polymerization it is possible to use high-energy electro-magnetic rays, mechanical energy, or the customary chemical polymerization initiators, such as organic peroxides, e.g., benzoyl peroxide, tert-butyl hydro-peroxide, methyl ethyl ketone peroxide, cumene hydroperoxide, dilauroyl peroxide or azo initiators, such as azodiisobutyronitrile (AIBN), for example.

[0095] Likewise suitable are inorganic peroxy compounds, such as (NH₄)₂S₂O₈, K₂S₂O₈ or H₂O₂, for example, where appropriate in combination with reducing agents (e.g., sodium hydrogensulfite, ascorbic acid, iron(II) sulfate, etc.) or redox systems comprising as reducing component an aliphatic or aromatic sulfonic acid (e.g., benzenesulfonic acid, toluenesulfonic acid, etc.).

[0096] The polymerization reaction can be conducted, for example, as a precipitation polymerization, emulsion polymerization, bulk polymerization, solution polymerization or gel polymerization. Particularly advantageous for the profile of properties of the copolymers of the invention is precipitation polymerization, preferably in tert-butanol.

[0097] The polyfunctional polymers of the invention possess a great structural diversity and, consequently, broad potential possibilities for use, which can be tailored to virtually any task where interface effects and/or surface effects play a part. Attention is drawn in particular to the high potential for application in the field of cosmetology, e.g., as thickeners and emulsifiers. The term “custom-tailored polymers” vividly describes the possibilities which this new class of polymer provides to the user.

[0098] The following examples serve to illustrate the invention without, however, restricting it thereto.

EXAMPLE 1

[0099] Reactants amount (g) NH₃-neutralized AMPS 80 Genapol-LA-070-methacrylate 10 Monofunctionalized ethoxylated siloxane 10 (methacrylic, ® Silvet 7608 WITCO) TMPTA 1.8 t-Butanol 500 Dilauroyl peroxide (initiator) 1

[0100] The polymer was prepared by the precipitation method in tert-butanol. The monomers in t-butanol were introduced as an initial charge and the reaction mixture was rendered inert, and then, after initial heating, the reaction was initiated by addition of DLP. The polymer was isolated by removing the solvent under suction and by subsequent vacuum drying.

EXAMPLE 2

[0101] Reactants amount (g) NH₃-neutralized AMPS 70 N-Vinylpyrrolidone 5 ® Genapol-T-250 methacrylate 15 [2-(Methacryloyloxy)ethyl]trimethylammonium chloride 10 Water 500 Na₂S₂O₈ (initiator) 1 Poly-N-vinylpyrrolidone ( ® K-30, BASF) 10

[0102] The polymer was prepared by the gel polymerization method in water. The monomers were dissolved in water, the reaction mixture was rendered inert, and then, after initial heating, the reaction was initiated by addition of sodium peroxodisulfate. The polymer gel was subsequently comminuted and the polymer was isolated by vacuum drying.

EXAMPLE 3

[0103] Reactants amount (g) AMPS 60 ® Genapol-BE-020 methacrylate 10 ® Genapol-T-250 acrylate 10 [2-Methacrylamido)ethyl]trimethylammonium chloride 20 Cyclohexane 200 Water 300 Span 80 1 Na₂S₂O₈ (initiator) 1

[0104] The polymer was prepared by the emulsion method in water. The monomers were emulsified in water/cyclohexane using ®Span 80, the reaction mixture was rendered inert using N₂, and then, after initial heating, the reaction was initiated by addition of sodium peroxodisulfate. The polymer emulsion was subsequently evaporated down (cyclohexane acting as azeotrope former for water) and by this means the polymer was isolated.

EXAMPLE 4

[0105] Reactants amount (g) NH₃-neutralized AMPS 60 ® PEG-750 methacrylate 20 Methacryloyloxypropyldimethicone ( ® GP-478, 10 Genesee Pol. Corp.) Perfluoroctyl polyethylene glycol methacrylate 10 t-Butanol 500 AIBN (initiator) 1 Poly[N-vinylcaprolactone-co-acrylic acid] (10/90) 10

[0106] The polymer was prepared by the precipitation method in tert-butanol. The monomers in t-butanol were introduced as an initial charge and the reaction mixture was rendered inert, and then, after initial heating, the reaction was initiated by addition of AIBN. The polymer was isolated by removing the solvent under suction and by subsequent vacuum drying.

EXAMPLE 5

[0107] Reactants amount (g) Na-neutralized AMPS 80 N-Vinylformamide 5  ®Genapol-O-150 methacrylate 5 Diallyldimethylammonium chloride (DADMAC) 10 Water 300 TMPTA 1.8 H₂O₂/iron (initiator) 1 Poly[N-vinylformamide] 8

[0108] The polymer was prepared by the solution method in water. The monomers were dissolved in water, the reaction mixture was rendered inert, and then, after initial heating, the reaction was initiated by means of a suitable redox couple. The polymer solution was subsequently evaporated down and the polymer was then isolated by vacuum drying.

EXAMPLE 6

[0109] Reactants amount (g) NH₃-neutralized AMPS 70 ® Genapol-T-250 acrylate 10 N-Methyl-4-vinylpyridinium chloride 5 Monofunctionalized (methacrylically) ethyoxylated siloxane 2.5 ( ® Silvet Y-12867, WITCO) Perfluorohexyl polyethylene glycol methacrylate 2.5 Polyethylene glycol dimethacrylate (M_(n) = 5 000 g/mol) 10 t-Butanol 500 Dilauroyl peroxide 2 Poly[N-vinylcaprolactam] 4

[0110] The polymer was prepared by the precipitation method in tert-butanol. The monomers in t-butanol were introduced as an initial charge and the reaction mixture was rendered inert, and then, after initial heating, the reaction was initiated by addition of DLP. The polymer was isolated by removal of the solvent under suction and by subsequent vacuum drying.

EXAMPLE 7

[0111] Reactants amount (g) NH₃-neutralized AMPS 10 Acrylamide 20 N-2-Vinylpyrrolidone 30 Monofunctionalized (methacrylically) ethyoxylated 20 Siloxane ( ® Silvet 7608 WITCO) Methacryloyloxypropyldimethicone ( ® GP-446, 10 Genesee Pol. Corp.)  ®Fluowet AC 812 10 t-Butanol 500 Dilauroyl peroxide 2

[0112] The polymer was prepared by the solution method in tert-butanol. The monomers in t-butanol were introduced as an initial charge, the reaction mixture was rendered inert, and then, after initial heating, the reaction was initiated by addition of DLP. The polymer was isolated by evaporation of the solvent and by subsequent vacuum drying.

EXAMPLE 8

[0113] Reactants amount (g) NH₃-neutralized AMPS 60 Diallyldimethylammonium chloride (DADMAC) 10 [2-(Methacryloyloxy)ethyl]trimethylammonium chloride 10  ®Genapol-LA-250 crotonate 10 Methacryloyloxypropyldimethicone ( ® GP-478, 10 Genesee Pol. Corp.) Isopropanol 300 Water 200 Potassium peroxodisulfate 2 Poly[acrylic acid-co-N-vinylformamide] 7

[0114] The polymer was prepared by the solution method in an isopropanol/water mixture. The monomers were introduced in isopropanol/water, the reaction mixture was rendered inert, and then, after initial heating, the reaction was initiated by addition of potassium peroxodisulfate. The polymer was isolated by evaporation of the solvent mixture and by subsequent vacuum drying. 

What is claimed is:
 1. A water-soluble or water-swellable copolymer obtainable by free-radical copolymerization of A) acryloyldimethyltaurine and/or acryloyldimethyltaurates, B) if desired, one or more other olefinically unsaturated, noncationic, optionally crosslinking comonomers containing at least one oxygen, nitrogen, sulfur or phosphorus atom and possessing a molecular weight of less than 500 g/mol, C) if desired, one or more olefinically unsaturated, cationic comonomers containing at least one oxygen, nitrogen, sulfur or phosphorus atom and possessing a molecular weight of less than 500 g/mol, D) if desired, one or more at least monofunctional, silicon-containing components capable of free-radical polymerization, E) if desired, one or more at least monofunctional, fluorine-containing components capable of free-radical polymerization, F) if desired, one or more mono- or polyolefinically unsaturated, optionally crosslinking macromonomers each possessing at least one oxygen, nitrogen, sulfur or phosphorus atom and having a number-average molecular weight of greater than or equal to 200 g/mol, the macromonomers not being a silicon-containing component D) or fluorine-containing component E), G) the copolymerization taking place in the presence or absence of at least one polymeric additive having number-average molecular weights of from 200 g/mol to 10⁹ g/mol, H) with the proviso that component A) is copolymerized with at least two components selected from at least two of the groups C) to F).
 2. The copolymer as claimed in claim 1, wherein the comonomers B) comprise unsaturated carboxylic acids, salts of unsaturated carboxylic acids, anhydrides of unsaturated carboxylic acids, esters of unsaturated carboxylic acids with aliphatic, olefinic, cycloaliphatic, arylaliphatic or aromatic alcohols having 1 to 22 carbon atoms, open-chain N-vinyl amides, cyclic N-vinyl amides having a ring size of from 3 to 9, amides of acrylic acid, amides of methacrylic acid, amides of substituted acrylic acids, amides of substituted methacrylic acids, 2-vinylpyridine, 4-vinylpyridine, vinyl acetate; styrene, acrylonitrile, vinyl chloride, vinylidene chloride, tetrafluoroethylene, vinylphosphonic acid or the esters or salts thereof, vinylsulfonic acid or the esters or salts thereof, allylphosphonic acid or the esters or salts thereof and/or methallylsulfonic acid or the esters or salts thereof.
 3. The copolymer as claimed in claim 1 and/or 2, wherein the comonomers C) comprise diallyldimethylammonium chloride, [2-(methacryloyloxy)ethyl]trimethylammonium chloride, [2-(acryloyloxy)ethyl]trimethylammonium chloride, [2-methacrylamidoethyl]trimethylammonium chloride, [2-(acrylamido)ethyl]trimethylammonium chloride, N-methyl-2-vinylpyridinium chloride and/or N-methyl-4-vinylpyridinium chloride.
 4. The copolymer as claimed in at least one of claims 1 to 3, wherein the silicon-containing components D) are compounds of the formula (I) R¹—Z—[(Si(R³R⁴)—O—)_(w)—(Si(R⁵R⁶)—O)_(x)—]—R²  (I) where R¹ represents a vinyl, allyl, methallyl, methylvinyl, acryloyl, methacryloyl, crotonyl, senecionyl, itaconyl, maleyl, fumaryl or styryl radical; Z is a chemical bridge, preferably selected from —O—, —((C₁-C₅₀)alkylene)-, —((C₆-C₃₀)arylene)-, —((C₅-C₈)cycloalkylene)-, —((C₁-C₅₀)alkenylene)-, -(polypropylene oxide)_(n)-, -(polyethylene oxide)_(o), -(polypropylene oxide)_(n)-(polyethylene oxide)_(o), where n and o independently of one another denote numbers from 0 to 200 and the distribution of the EO/PO units can be random or in the form of blocks, —((C₁-C₁₀)alkyl)-(Si(OCH₃)₂)— and —(Si(OCH₃)₂)—; R³, R⁴, R⁵, and R⁶ independently of one another are —CH₃, —O—CH₃, —C₆H₅ or —O—C₆H₅; w, x denote numbers from 0 to 500, it being necessary for either w or x to be greater than zero; and R² is a saturated or unsaturated aliphatic, cycloaliphatic, arylaliphatic or aromatic radical having in each case 1 to 50 carbon atoms or a group of the formulae —OH, —NH₂, —N(CH₃)₂, —R⁷ or a group —Z—R¹, where Z and R¹ are as defined above and R⁷ is a group of the formula —O—Si(CH₃)₃, —O—Si(phenyl)₃, —O—Si(O—Si(CH₃)₃)₂CH₃ or —O—Si(O—Si(Ph)₃)₂Ph.
 5. The copolymer as claimed in at least one of claims 1 to 4, wherein the fluorine-containing components E) are compounds of the formula (II) R¹—Y—C_(r)H_(2r)C_(s)F_(2s)CF₃  (II) where R¹ represents a polymerizable function from the group of the vinylically unsaturated compounds, preferably a vinyl, allyl, methallyl, methylvinyl, acryloyl, methacryloyl, crotonyl, senecionyl, itaconyl, maleyl, fumaryl or styryl radical; Y is a chemical bridge, preferably —O—, —C(O)—, —C(O)—O—, —S—, —O—CH₂—CH(O—)—CH₂OH, —O—CH₂—CH(OH)—CH₂—O—, —O—SO₂—O—, —O—S(O)—O—, —PH—, —P(CH₃)—, —PO₃—, —NH—, —N(CH₃)—, —O—(C₁-C₅₀)alkyl-O—, —O-phenyl-O—, —O-benzyl-O—, —O—(C₅-C₈)cycloalkyl-O—, —O—(C₁-C₅₀)alkenyl-O—, —O—(CH(CH₃)—CH₂—O)_(n)—, —O—(CH₂—CH₂—O)_(n)—, and —O—([CH-CH₂—O]_(n)—[CH₂—CH₂—O]_(m))_(o)-, where n, m, and o independently of one another denote numbers from 0 to 200; and r, s are stoichiometric coefficients which independently of one another can be numbers between 0 and
 200. 6. The copolymer as claimed in at least one of claims 1 to 5, wherein the macromonomers F) are compounds of the formula (III) R¹—Y—[(A)_(v)—(B)_(w)—(C)_(x)—(D)_(z)]—R²  (III)where R¹ represents a polymerizable function from the group of the vinylically unsaturated compounds, preferably a vinyl, allyl, methallyl, methylvinyl, acryloyl, methacryloyl, crotonyl, senecionyl, itaconyl, maleyl, fumaryl or styryl radical; Y is a bridging group, preferably —O—, —S—, —C(O)—, —C(O)—O—, —O—CH₂—CH(O—)—CH₂OH, —O—CH₂—CH(OH)—CH₂—O—, —O—SO₂—O—, —O—SO₂—O—, —O—SO—O—, —PH—, —P(CH₃)—, —PO₃—, —NH—, and —N(CH₃)—; A, B, C, and D independently of one another are discrete chemical repeating units, preferably originating from acrylamide, methacrylamide, ethylene oxide, propylene oxide, AMPS, acrylic acid, methacrylic acid, methyl methacrylate, acrylonitrile, maleic acid, vinyl acetate, styrene, 1,3-butadiene, isoprene, isobutene, diethylacrylamide, and diisopropylacrylamide, more preferably ethylene oxide or propylene oxide; v, w, x, and z independently of one another amount to from 0 to 500, preferably from 1 to 30, the sum of v, w, x, and z being on average ≧1; and R² is a linear or branched aliphatic, olefinic, cycloaliphatic, arylaliphatic or aromatic (C₁-C₅₀) hydrocarbon radical, OH, —NH₂ or —N(CH₃)₂ or is [—Y—R¹].
 7. The copolymer as claimed in at least one of claims 1 to 6, wherein the polymeric additives G) are homopolymers and copolymers of N-vinylformamide, N-vinylacetamide, N-vinylpyrrolidone, ethylene oxide, propylene oxide, acryloyl-dimethyltaurine, N-vinylcaprolactone, N-vinylmethylacetamide, acrylamide, acrylic acid, methacrylic acid, N-vinylmorpholide, hydroxymethyl methacrylate, diallyl-dimethylammonium chloride (DADMAC) and/or [2-(methacryloyloxy)ethyl]trimethyl-ammonium chloride (MAPTAC); polyalkylene glycols and/or alkylpolyglycols.
 8. The copolymer as claimed in at least one of claims 1 to 7, wherein the copolymerization takes place in the presence of at least one polymeric additive G).
 9. The copolymer as claimed in at least one of claims 1 to 8, which is crosslinked.
 10. The copolymer as claimed in at least one of claims 1 to 9, prepared by precipitation polymerization in tert-butanol. 